Polymer modified engineered cement concentrate for making high strength floor leveling beds which are self curing intended for interior and exterior underlays.
Dry Mortar Density=1000 – 1100 kg/m3
Pot Life=4 Hours
Time for Foot Traffic= ≥ 24
Time for Heavy Traffic= ≥ 72 Hours
Advantages:
- • High strength
- Shock & impact resistant
- Water retaining & self curing
- Non-Shrink
- Easy to use
- Complies with EN 13813 under CT-C25F3B1.5SH40 classification.
Substrates:
- Concrete
- Cement mortar beds
- Cement Terrazo
STONEMIX PLAST CEMis a Eco-friendly, hydraulic, normal-setting, rapid-drying mineral binder for highperformance screeds and heat-radiant slabs, STONEMIX PLAST CEM, mixed with inert materials of assorted grain size from 0 to 8 mm, creates screeds of high dimensional stability and constant moisture stability, guaranteeing the rapid safe laying of ceramic tiles after 24 hours and hardwood floors after just 5 days.
Appearance=Mixture of binders
Mixing water=Up to 12 Lit / bag 25 kg
Pot life=>3 hours
Temperature range for application=from + 5˚C to +45˚ C
Fool traffic=8 - 12 hours
Advantages:
- For internal and external use
- Low water/cement ratio
- Mechanical performances superior to those of Portlandcements High dimensional stability and long-lasting performance
- Prolonged workability both in the manual and mechanical laying
- Suitable for laying homogeneous tiles natural stone, hardwood floors and resilient materials using adhesives
STONEMIX PLAST SL is a fast hardening and drying cementitious self-leveler for thicknesses from 3mm to 30 mm fiber-reinforced for interiors and exteriors product with low content of volatile organic compounds (VOC). It is a high fluid, self-leveling product of high dispersing effect(HDE) technology that creates perfectly plane substrate. The substrate has extra rapid hardening and self leveling which lives with rheological fluidity and dynamism.
Appearance=Grey in colour, Ready- Mixed
Mixing Water=4 - 4.5 liters / Bag of 25 Kg EN 12706
Pot Life =≥ 45 Min.
Gel Time (Self-Leveling]=≥ 40 Min.
Temperature Range For Application=From +5 °C to +30 °C
Min. Thickness=≥ 3mm
Max. Thickness Obtainable=≤ 30 mm
Fool Traffic *=Achievable After 12 hours
Advantages:
- Excellent self-leveling capacity.
- Fast hardening and drying time.
- High mechanical flexural and compressive strength
- High bond strength on conventional cementitious substrates
- No shrinkage
- Excellent abrasion resistance
Substrates:
- STONEMIX PLAST SL is suitable for internal & external uses for high resistance correcting (3mm to 30mm) of irregular and undulated substrates to be made ready for ceramics, homogeneous tiles, marbles parquet and resilient materials.
STONEMIX PLAST LEVEL is a high-performance levelling of substrates from 1 to 10 mm thickness, with normal setting prolonged workability, manufactured by CERTESTONE PERFORMANCE CHEMICALS LLP, suitable for subsequent laying of tiles after 12-24 hours and for laying of natural stone, parquet and resilient materials 3-5 days after application, at +23 C 50% R.H. Apply using a smooth spreader on the previously prepared, clean and dimensionally stable substrate and finish with a rigid float.
Appearance=Ready-mixed
Mixing Water=6.5 Ltr. / 25 Kg
Pot Life=> 4 h
Gel Time (Self-Leveling)=> 40 min.
Temperature range for application=from +5 C to +45 C
Min. Thickness=> 1 mm
Max. Thickness Achievable=>10 mm
Foot Traffic=24 hours
Advantages:
- Thixotropic.
- Eco-friendly.
- Normal setting.
- Correction and extended workability of irregular substrates.
- Exceeds ANSI A118.4 shear bond strength requirements
- Extended workability.
- Guranteeing the correction of large surfaces even in extreme climatic conditions with a smooth finish which ideal for the subsequent laying of covering using Cretestone adhesives.
Substrates:
- Internal & External.
- Also suitable for large surface areas.
- High level of slide for fast and safe applications.
- High dimentional stability and long lasting performance.
- High mechanical resistance.
- Suitable for laying ceramic tiles, porcelian tiles, natural.
- floors and resilient materials using adhesives.
- Cement Backer Board**